Mig Welding Copper Pipe

If the copper is thicker you will need to adjust the gas and amp by applying helium and upping the.

Mig welding copper pipe.

Copper and its alloys are widely used in construction especially. Use the proper gas ratio. As a general rule of thumb copper under 2 mm should have argon gas and up to 160 a applied. In this video rob will go over how to properly tig weld copper tubing with silver solder.

Avoid rolling up sleeves or pant cuffs as sparks or hot metal will deposit in the folds and may burn through the material. In welding copper sheets the heat is conducted away from the welding zone so rapidly that it is difficult to bring the temperature up to the fusion point. It is often necessary to raise the temperature level of the sheet in an area of 6 0 to 12 0 in. Depending on if you are using tig tungsten inert gas or mig metal inert gas and the thickness of your copper you will need to adjust the ratio of your gas and temperature.

Whereas mig welding requires a preheating of 10 100 c and up to 240 amps of power with argon as its shielding gas. Since the predominant application of copper nickels is in the form of relatively thin walled pipe the gas shielded tungsten arc welding process known as tig or gtaw is frequently used both for joining pipe sections and for attaching fittings and flanges. A welding procedure specification wps should be prepared in all cases. For example in welding copper with thickness of 5mm 0 196 inch tig welding requires a preheating of 50 c as well as shielding gas of argon helium and mix up to 300 amps of power.